calcium silicate thermal insulation materials

Enlarge

Member Type:
Post Date: Jul 18, 2008
Validity Date: Aug 1, 2008
Category: Construction & Decoration » Special Materials » Heat Insulation

» Recommend » Report Fraud

Description

A型矽酸鈣隔熱材料

Non-asbestos calcium silicate thermal insulation materials

1. 強度高：在容重相近時，它是無機硬質絕熱材料中最高的保溫材料。

2. 耐熱性：在使用溫度範圍内不變形。

3. 保溫隔熱性：導熱係數比其它硬質塊狀絕熱材料低。

4. 本公司產品為無石棉製品。

5. 適用於鋼鐵、石化、陶瓷、玻璃、水泥等各種爐窖的保溫，及電力、機械、電子、造船等行業的保溫隔熱。

1. High strength: the strongest one among the inorganic thermal insulation materials with the similar density.

2. Thermal-resistance: non-deformation at the temperature used.

3. Thermal insulation: lower thermal conductivity than other hard mass thermal insulation materials.

4. Asbestos-free.

5. products are recommended as thermal insulation in stove, cave dwelling of steel mill, petrochemical, ceramics, glass, cement industries and power industries as well as other various ancillary heating equipment.

產品主要技術性能 Technical characteristics
	單位 Unit	本公司標準 Our company				美國標準 ASTM-C533 Type-II	日本標準 JISA9510-1995		英國標準 BS3958-82
		A-13	A-17	A-22	A-28	美國標準 ASTM-C533 Type-II	I-13	II-22	英國標準 BS3958-82
密度 Density	Kg/m³	≤135	≤170	≤220	≤240	≤240	≤135	≤220	210~280
導熱係數 Thermal Conductivity	W/m·k	≤0.042	≤0.047	≤0.053	≤0.073	≤0.095 (204℃)	≤0.042	≤0.053	0.074 (200℃)
抗壓強度 Compressive Strength	MPa (Kgf/cm²)	≥0.30 (4.1)	≥0.40 (4.1)	≥0.50 (5.1)	≥0.50 (5.1)	≥0.414			≥0.35
抗折強度 Bending Strength	MPa (Kgf/cm²)	≥0.20 (2.0)	≥0.30 (3.0)	≥0.35 (3.5)	≥0.35 (3.5)	≥0.31	≥0.2	≥0.31	≥0.25 (3.1)
線收縮率 Linear Shrinkage	%	≤2.0	≤2.0	≤2.0	≤2.0	≤2.5	≤2.0	≤2.0	≤2.0
最高使用溫度 Max. Service Temp.	K (℃)	(1000)	(1000)	(1000)	(1000)	982	1000	1000	950
含水率 Moisture Content	%	≤6.0	≤6.0	≤6.0	≤6.0	≤6.0